Using pressing under high pressure, proposed by Vl. Oganov, we obtain solid samples from a stoichiometric mixture of different materials. After further high-temperature processing, transparent crystals were obtained. Gd3In2Ga3O12 crystals were synthesized in this way. The composition of the crystals was checked using a DRON-2 X-ray machine. Under the influence of an x-ray tube with α silver anode k α1 E = 22.169 keV, k α2 E = 21.99keV, and Kβ E = 22.94 keV, the scaling properties of the crystals were observed. This work continues. The technology of obtaining Ag and Cu nanoparticles in colloidal solution was developed, due to which it was possible to obtain a metal-carbon composite based on cotton fabric.