Experimental Physics Division №260

Using pressing under high pressure, proposed by Vl. Oganov, we obtain solid samples from a stoichiometric mixture of different materials. After further high-temperature processing, transparent crystals were obtained. Gd3In2Ga3O12 crystals were synthesized in this way. The composition of the crystals was checked using a DRON-2 X-ray machine. Under the influence of an x-ray tube with α silver anode k α1 E = 22.169 keV, k α2 E = 21.99keV, and Kβ E = 22.94 keV, the scaling properties of the crystals were observed. This work continues. The technology of obtaining Ag և Cu nanoparticles in colloidal solution was developed, due to which it was possible to obtain a metal-carbon composite based on cotton fabric.